ELECTRODEPOSITION OF COPPER NANOWIRES IN POROUS POLYCARBONATE MEMBRANES
Abstract
Copper nanowires of diameter 50 nm have been synthesized by electrochemical deposition in a nanoporous polycarbonate template. These membranes were created by ion irradiation of 30 μm thick polycarbonate foils at UNILAC accelerator of GSI, Germany. Subsequent chemical etching of these foils were carried out in PINSTECH using 6M NaOH solution at 50 oC. A thin Cu layer on one side of these membranes, deposited by thermal evaporation, acted as cathode. A Cu rod was used as anode and the deposition was carried out potentiostatically at room temperature in a two electrode electrochemical cell. Subsequent to fabrication, the wires were characterized by scanning electron microscopy (SEM), X-ray diffraction (XRD) and UV-Visible spectroscopy.References
T.W. Cornelius, M.E. Toimil-Molares, S. Karim and R. Neumann, Phys. Rev. B 77 (2008) 125425.
B. Wu, A. Heidelberg and J.J. Boland, Nat. Mater. 4 (2005) 525.
B. Wu, A. Heidelberg, J.J. Boland, J.E. Sader, X-M. Sun and Y.D. Li, Nano Lett. 6 2005) 468.
Y. Xia, P. Yang, Y. Sun, Y. Wu, B. Mayers, B. Gates, Y. Yin, F. Kim and H. Yan, Adv. Mater. 15 (2003) 353.
S. Karim, M.E. Toimil-Molares, A. G. Balogh, W. Ensinger, T. W. Cornelius, E. U. Khan and R. Neumann, Nanotechnology 17 (2006) 5954.
M.E. Toimil-Molares, A.G. Balogh, T.W. Cornelius, R. Neumann and C. Trautmann, Appl. Phys. Lett. 85 (2004) 5337.
T. R. Kline, M. Tian, J. Wang, A. Sen, M. W. H. Chan and T. E. Mallouk, Inorg. Chem. 45 (2006) 7555.
S. Matsui and Y. Ochiai, Nanotechnology 7 (1996) 247.
S.-K. Eah, H. M. Jaeger, N. F. Schererb, G. P. Wiederrecht and X.-M. Linc, Appl. Phys. Lett. 86 (2005) 31902.
J. J. Mock, S. J. Oldenburg, D. R. Smith, D. A. Schultz and S. Schultz, Nano Lett. 2 (2002) 465.
J. Takahara, S. Yamagishi, H. Taki, A. Morimoto and T. Kobayashi, Opt. Lett. 22 (1997) 475.
M. Derouard, J. Hazart, G. Lérondel, R. Bachelot, P.-M. Adam and P. Royer, Opt. Express 15 (2007) 4238.
C.R. Martin, Science 266 (1993) 1961.
J. Wang, M. Tian, T.E. Mallouk and M.H.W. Chan, J. Phys. Chem. B 108 (2004) 841.
C. Ji and P.C. Searson, Appl. Phys. Lett. 81 (2002) 4437.
A. Huczko, Appl. Phys. A 70 (2000) 365.
R.C. Furneaux, W.R. Rigby and A.P. Davidson Nature 337 (1989)147.
S. Karim, W. Ensinger, T.W. Cornelius and R. Neumann, Physica E 40 (2008) 3173.
T.W. Cornelius, M.E. Toimil-Molares, S. Karim and R. Neumann, J. Appl. Phys. 100 (2006) 114307.
P. Apel, Radiat. Meas. 34 (2001) 559.
P. Apel, I.V. Blonskaya, O.L. Orelovich, S.N. Akimenko, B. Sartowska and S.N. Dmitriev, Coll. Jour. 66 (2004) 725.
S-Y. Yim, H-G. Ahn, K-C. Je1, M. Choi, C.W. Park, H. Ju and S-H. Park, Opt. Express 15 (2007) 10282.
M.E. Toimil-Molares, J. Brötz, V. Buschmann, D. Dobrev, R. Neumann, R. Scholz, I.U. Schuchert, C. Trautmann and J. Vetter, Nucl. Instrum. Methods Phys. Res. B. 185 (2001) 192.
D. Dobrev, J. Vetter, N. Angert and R. Neumann, Appl. Phys. A 69 (1999) 233.
S. Karim, M.E. Toimil-Molares, F. Maurer, G. Miehe, W. Ensinger, J. Liu, T.W. Cornelius and R. Neumann, Appl. Phys. A 84 (2006) 403.
X. W. Wang, G. T. Fei, X. J.Xu, Z. Jin and L.D. Zhang, J. Phys. Chem. B 109 (2005) 24326.
H. Pan, H. Sun, C. Poh, Y. Feng and J. Lin, Nanotechnology 16 (2005)1559.
M.E. Toimil-Molares, V. Buschmann, D. Dobrev, R. Neumann, R. Scholz, I.U. Schuchert and J. Vetter, Adv. Mater. 13 (2001) 62.
T. Gao, G. W. Meng, Y. Wang, S. Sun and L. D. Zhang, J. Phys.: Condens. Matter 14 (2002) 355.
J. Liu, J. L. Duan, M. E. Toimil-Molares, S. Karim, T. W. Cornelius, D. Dobrev, H. J. Yao, Y. M. Sun, M. D. Hou, D. Mo, Z. G. Wang and R. Neumann, Nanotechnology 17 (2006) 1922.
F. Maurer, J. Brötz, S. Karim, M. E. Toimil-Molares, C. Trautmann and H. Fuess, Nanotechnology 18 (2007) 135709.
J. L. Duan, T. W. Thomas, J. Liu, S. Karim, H. J. Yao, O. Picht, M. Rauber, D. Dobrev, S. Müller, C. Trautmann and R. Neumann, Crys. Growth. Design (submitted).
L. Barnes, A. Dereux and T. W. Ebbesen, Nature 424 (2003) 824.
U. Kreibig and M. Vollmer, Optical Properties of Metal Clusters (Springer, 1995) Chap. 2.